Causes of transverse cracks in the corners of continuous casting slabs and preventive measures1. Transverse crackThis is a small transverse crack located at th
Causes of transverse cracks in the corners of continuous casting slabs and preventive measures
1. Transverse crack
This is a small transverse crack located at the corner of the cast slab. Produced at the troughs of the vibration marks on the inner arc surface of the cast slab, which are usually hidden and invisible. Transverse cracks co-exist with vibration marks. To reduce transverse cracks, it is necessary to reduce the depth of small vibration marks. Increase the vibration frequency and reduce the depth of vibration marks. The use of high frequency and small amplitude crystallizer vibration mechanism can effectively reduce the depth of vibration marks, Thereby reducing the occurrence of transverse cracks.
2. Causes of transverse cracks
1) The taper of the copper mould tube is too large.
2) The surface of the copper mould tube is scratched.
3) Inaccurate arc alignment between crystallizer outlet and zero section.
3 .Measures to prevent Transverse cracks
1) The crystallizer adopts high frequency (200～400 times/min) and small amplitude (2～4mm) is an effective way to reduce the depth of vibration marks.
2) The secondary cooling zone adopts smooth and weak cooling, and the surface temperature of the cast slab during straightening is greater than 900°C.
3) The liquid level of the crystallizer is stable, and the mold powder with good lubricating performance and low viscosity is used.
4) Use flame to clean surface cracks
shengmiao
Harm of too high temperature: when molten steel out of cooper mold, the billet shell is thin and easy to break out; The accelerated erosion of refractory can ea
shengmiao
1. The barrier function (mainly completed by the liquid slag layer) isolates the contact between air and molten steel, blocks the secondary oxidation of molten
shengmiao
In continuous casting, low corrosion resistance often occurs, which directly leads to uneven composition and will eventually affect the smelting quality. In or