Ultrasonic Testing Of Copper Mould CoatingsBecause the nickel alloy layer of copper mold of continues casting machine in steel mill, the adjoining surfaces of
Ultrasonic Testing Of Copper Mould Coatings
Because the nickel alloy layer of copper mold of continues casting machine in steel mill, the adjoining surfaces of mold in pouring gate due to the high temperature and the molten steel attrition creates the breakage or the peeling. Therefore use ultrasonic testing to pick out the bad adjoining surfaces of mold in time to avoid the nickel layer’s breakage. In the casting process, the breakage of copper mold tubes cause the cooling water contact with the molten steel creates BO. Thus cause not only the production loses but also creates the gas to explode and cause the personnel and the equipment dangerous loss.
RESULTS
1. Coating nickel layer of copper mold must serious control in the production system, otherwise easy to have the bonding problem.
2.The copper mold in different continues casting machine under the same condition of casting process, coating layer has the different result actually, therefore may suspect reasonably the casting machine has the sensitive factor cause fissure and dis-bonding of layer during the maintenance process, suitable further comparative analysis. To avoid the trend opportunity of fissure and dis-bonding of nickel layer of the copper mold by continually collect records, reorganizes the events condition, and seeks the process condition, the maintenance condition optimization.
CONCLUSION
To using UT testing for checking layer bonding condition of mold is important for prevent or reduce the fissure and dis-bonding probability in conti-casting production line.
shengmiao
Harm of too high temperature: when molten steel out of cooper mold, the billet shell is thin and easy to break out; The accelerated erosion of refractory can ea
shengmiao
1. The barrier function (mainly completed by the liquid slag layer) isolates the contact between air and molten steel, blocks the secondary oxidation of molten
shengmiao
In continuous casting, low corrosion resistance often occurs, which directly leads to uneven composition and will eventually affect the smelting quality. In or